glue dinitrol 410 uv gray 310ml

gluing + sealing
dinitrol 410 uv nf is used as an adhesive and sealant in the industrial production of buses, trucks and caravans and in shipbuilding. the material adheres perfectly to primed and painted metals, thermosets (glass fiber reinforced plastic, hard PVC), wood and glass.

dinitrol 410 uv nf
» reduced preparation and processing times
» very good UV stability and weather resistance
» saves pretreatment costs, as many substrates do not require adhesion promoters
» high acceptance due to user-friendly handling and high-quality finish reliable 1-component polyurethane long-term adhesive and sealant


dinitrol 410 uv nf is a 1-component polyurethane sealant and adhesive with good durability and UV stability.
the sealant is fast drying and flexible and can be covered with most colors. 2-c acrylic paints can be applied wet-on-wet. colors it
the content of alcohol and alkyd resins makes curing difficult.

application
dinitrol 410 uv nf is used for bonding and sealing in many industrial areas such as bus, truck and motorhome manufacturing. the material adheres well to primed and painted metals, thermosets (glass fiber reinforced plastic and hard PVC), wood and glass.
it is suitable for sealing overlapping and expansion joints in visible interior and exterior areas in commercial vehicle manufacturing.
before applying to complex substrates, we recommend performing an adhesion test.

surface pretreatment
the treated surface must be clean, dry and free of dust, oil and grease. use dinitrol 582 / 580 to clean dirty surfaces. more information on its use
For dinitrol pretreatment products, see our technical data or dinitrol pretreatment table.

application
we recommend applying the adhesive sealant with a standard application gun (eg dinitrol mastertool). for easy processing process the glue at room temperature. warmer temperatures and increasing air humidity shorten the drying time, colder temperatures and lower air humidity increase the drying time.

can be painted over
dinitrol 410 uv nf can be painted over with most colors after curing.


raw material base polyurethane, prepolymer
flow rate (2.6 mm/2.8 bar 20°c) 40-60 g/min cartridge
density ~ 1.2 g/ml
processing temperature + 5 °c to + 35 °c
temperature tolerance - 40 °c to + 90 °c (short-term up to 120 °c)
resistance to water, salt water, dilute acids and alkalis, water-based cleaning agents
short-term gasoline, grease and mineral oil
curing hardens when exposed to moisture.
film formation time ~ 30 min (23 °c / 50% room temperature)
surface drying ~ 2.5 h (non-sticky)
curing rate ~ 3 mm per 24 hours (at 23 °c / 50% RH)
shore a hardness > 45
tensile strength (din 53504) 1.4 n / mm²
tear resistance (din 53504) ~ 8 n mm
elasticity (din 53504) 450%
modulus of elasticity (din 53504) 100% ~ 1.0 n/mm² after 24 hours.
cleaning unhardened material: gasoline
hardened material: can only be used for mechanical removal.