thread lock 10g

description
optimal thread locking product. can be used on oiled surfaces and galvanized screws.

characteristics
- resistant to tension and vibration
- good chemical resistance to gasoline, oil,
water/glycol, brake fluid
- adheres well to vertical surfaces
- drying without oxygen (anaerobic)
- prevents leaks
- can be used on oily surfaces

technical specifications
mold liquid
breaking torque 16 nm
DIN EN 15865
prevailing torque 10 nm
DIN EN 15865
chemical resistance relatively well withstood
oils, gasoline,
antifreeze, water and
brake fluid
initial strength 2-10 min (active);
10-60 min (passive)
functional strength 2-3 h
final strength 12 h
operating temperature
scope
-60 to 150 °C
thread friction value 0.13
compressive shear strength 16 n/mm²
DIN EN 15337
base dimethacrylate ester
density 1.1 g/cm³
DIN EN 542
color / appearance blue
the smell is characteristic
viscosity at 23 °c 1000 mpas
shelf life in original packaging
container
24 months
recommended storage space
temperature
8-21 °C

areas of use
used for all commonly used screw and nut sizes and
all classes.

application
apply evenly to bolts and nuts. the paste hardens
lack of air (anaerobic). during curing, a distinction must be made between active and passive materials. active materials generally refer to metals with a high iron or copper content (eg iron, steel, copper, brass, bronze). active materials ensure fast curing. passive materials such as high-alloy (stainless) steel, zinc, aluminum or plastic harden very slowly.

comment
due to its anaerobic properties, there must always be enough air in the bottle. otherwise the glue may harden prematurely. therefore, the bottle should only be filled about 1/3 full. however, the quantity always corresponds to the contents indicated on the container.